VALOX(沙伯基础)DR51/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX DR51 PBT是一种加15% GR聚酯，优异的机械、热和电气性能。无焰阻燃,射灯，电器外壳，把手，连接器。
 |
沙伯基础创新塑料的VALOX DR51 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)DR51/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 90 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 90 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 5900 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 140 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 140 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4500 | MPa | ASTM D 790 | |
| Hardness, Rockwell R | 118 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 95 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 5 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5100 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 100 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 30 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 27 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 330 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 330 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 40 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 40 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -20°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 4 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 4 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 4 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, annealed | 193 | °C | ASTM D 648 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.16E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.58E-05 | 1/°C | ASTM E 831 | |
| CTE, 60°C to 138°C, flow | 2.16E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 3.35E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.06E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 3.4E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.83E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 205 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.45 | - | ASTM D 792 | |
| Specific Volume | 0.71 | cm³/g | ASTM D 792 | |
| Filler Content | 17 | % | ASTM D 229 | |
| Water Absorption, 24 hours | 0.07 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 1.5-3.2 mm | 0.4-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2-4.6 mm | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 0.8-1.1 | % | SABIC method | |
| Melt Flow Rate, 265°C/5.0 kgf | 80 | g/10 min | ASTM D 1238 | |
| Density | 1.45 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Flow Rate, 250°C/2.16 kg | 18 | g/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 15 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 43 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 65 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 170 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 19.6 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23.2 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 300 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.75 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：13577 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：11657 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：11197 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：9383 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：8215 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：8169 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7612 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：7057 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：6933 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6710 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6656 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6507 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：6406 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6341 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：6314
推荐文章
-
PC(聚碳酸酯)TC621|科思创(Covestro AG)|物性表参数
科思创(Covestro)Makrolon(模克隆)PC TC621是一种导热性聚碳酸酯，密度(23°C)是1.42克/厘米³，导热系数是16/W/m/K，阻燃性能，熔体温度300℃，应用于光组件;LED散热片(金属替换);散热部件。以下是PC(聚碳酸酯)TC621|科思创(Covestro AG)|物性表参数物理性能额定值单位制测试方法密度 (23°C)1.42g/cm³ISO 1183收缩率ISO
-
塞拉尼斯TPV 8191-60B500|SANTOPRENE物性表参数
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 8191-60B500是一种热塑性硫化弹性体，8191-60B500也是一种柔软，黑色，特种热塑性硫化胶(TPV)。在要求硬/软组合的应用中，它特别适用于粘结pa6、pa6 /6、pa6 GF、pa11、pa12和pa6 /12，这种级别的山托丁烯TPV是剪切依赖的，可以在传统的热塑性塑料设备上进行注射成型或挤压加工，它
-
TPX(PMP共聚物)DX231|三井化学|物性表参数
三井化学TPX DX820是一种透明聚甲基戊烯共聚物(PMP共聚物)材料，由于吸水率极其低，因此有必要使用蒸汽减少的细菌，折射率为1.463 nd20，仅次于氟树脂，低折射率材料可以在医疗仪器和动物器械等方面使用。 TPX DX231物性表参数
-
PP(聚丙烯)RP315M/利安德巴塞尔/物性表参数
利安德巴塞尔(Lyondellbasell)Moplen PP RP315M是一种微改性聚丙烯无规共聚物，熔体流动速率(230°C/2.16kg)是8克/10分钟，密度(23°C)是0.9克/厘米³，Moplen RP315M通常被客户用于制造无取向铸造薄膜，客户报告固定，层压，纺织和食品包装的典型应用，客户反映，moplen RP315M具有非常好的加工性，用moplen RP315M生产的
-
PA66(尼龙66)HS2350B/LG化学/物性表参数
PA66 HS2350B LUMID是LG化学开发的PA66化合物的商品名，性能是无氯/无溴阻燃，高耐热,用于汽车/底盘/发动机/气缸盖罩。以下是PA66(尼龙66)HS2350B/LG化学/物性表参数基本信息原厂资料产品特性热稳定填充增强添加助剂热稳定剂成型方式注塑增强填充35% 玻纤技术参数物理性能值/单位测试标准测试条件密度1.4 g/cm³ISO 1
-
PBT(聚对苯二甲酸丁二酯)5010GN1-15AM|三菱塑料|物性表参数
三菱工程塑料NOVADURAN PBT 5010GN1-15AM是一种聚对苯二甲酸丁二酯(PBT)材料，熔融体积流量（MVR)(cm³/10min)是40((250°C/5.0kg))，简支梁缺口冲击强度(kJ/m²)是6.0(23°C)，UL阻燃等级是V-0(0.71mm)，含有的填充物为33%玻璃纤维增强材料，加工方式为：注射成型，NOVADURAN 5010GN1-15AM主要特性为:阻燃/额定火焰。以
-
TPU(热塑性聚氨酯)D11H92S/路博润(Lubrizol)物性表参数
路博润(Lubrizol)Pearlthane TPU D11H92S是一种以聚己内酯共聚酯为基础的热塑性聚氨酯，肖氏硬度92A，特点是优异的流动性能和机械性能，出色的低压缩设定值和耐高温性能，本系列旨在满足对广泛技术应用日益严格的需求，例如高柔韧性薄膜、耐磨软管、柔软注塑部件或特殊化合物，主要用于注塑成型应用。以下是TPU(热塑性聚氨酯
-
PA46(尼龙46)TS241B3/荷兰DSM/物性表参数
荷兰DSM帝斯曼Stanyl聚合物PA46 TS241B3是一款加入15%碳黑增强，润滑剂，注塑成型的PA46原料，应用于电子电气，Stanyl作为高性能聚酰胺,在对耐热性、设计硬度、摩擦磨耗以及流动性都有要求的严苛的应用中表现优异，Stanyl能在高达220℃时依旧保持良好的机械性能，这使它比PPA、PA6T、PA9T、PPS 和LCP更适合超高性能应用。帝
-
PBT(聚对苯二甲酸丁二酯)VX10|东丽|物性表参数
东丽TORAYCON树脂PBT VX10是一种全球品级,非增强高冲击, 低翘曲聚对苯二甲酸丁二酯,由东丽利用其在聚酯聚合和树脂加固化合物领域的专业技术开发而成的（聚丁烯对苯二甲酸酯）是一种聚酯类热塑
-
PC(聚碳酸酯)LDS3735|三菱工程塑料|物性表参数
三菱工程塑料XANTAR PC LDS3735是镭雕级别的聚碳酸酯,体积熔融指数13厘米3/10分钟; 密度是1.24g/cm³，拉伸模量是2200MPa，维卡软化温度141°C, 特性是：激光标记 ;磷含量，低（到无） ;无溴阻燃性，被广泛地用于各种工业生产，如运动器械、汽车部件、光学仪器、机械、办公自动化设备和电子设备，获得了客户的广泛信赖和支持