VALOX(沙伯基础)830/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 830 PBT是一种加30% GR PBT+ PET，表面光洁度好,典型的应用是热风枪外壳组件、工业胶枪、电器外壳和把手。
 |
沙伯基础创新塑料的VALOX 830 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)830/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10500 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 205 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 205 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7400 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 140 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 215 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8800 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 174 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 123 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 60 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 55 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 800 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 800 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 90 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 90 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 3 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 9 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 10 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 10 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 60 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 208 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 200 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 208 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.7E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 1.97E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.59E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 1.51E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.42E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 208 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 208 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 202 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 120 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 120 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.55 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.4-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.2-1 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.6-1 | % | SABIC method | |
| Melt Flow Rate, 265°C/2.16kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 45 | g/10 min | ASTM D 1238 | |
| Density | 1.55 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.15 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 23 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 14 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 35 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 208 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 27 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.2 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.013 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 27 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.2 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0008 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.013 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 150 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260 - 285 | °C | ||
| Nozzle Temperature | 265 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 255 - 280 | °C | ||
| Rear - Zone 1 Temperature | 240 - 260 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 110 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：7660 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：7282 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：6051 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：5932 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：5397 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：4979 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：4617 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：4392 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：4382 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：4244 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：4216 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：4176 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：4052 -
PC(聚碳酸酯)PC-1100|乐天化学(LOTTE CHEMI···乐天化学的LOTTE Chemical HOPELEX PC PC-1100 是一种聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高强度、FDA/EU 食品容器认证，用于普通注塑产品。 以下是PC(聚碳酸酯)PC-1100/韩国乐天化学
浏览量：3983 -
Grilamid(瑞士EMS)TR55|PA12(尼龙12)物性表···瑞士(EMS)Grilamid PA12 TR55是一种基于十二内酰胺的高性能热塑性材料，经验证可用于众多高品质应用，并且已拥有40多年的应用经验。这些应用包括精密注塑成型（例如电子应用中的）、卫生洁具、燃油和空气制动系统管路及光纤波导护套,Grilamid TR等级是一种无定形热塑性塑料，其成分以一种独特方式组合了半结晶聚酰胺12和无定
浏览量：3940
推荐文章
-
Versaflex/G2708N/TPE物性表参数
美国普立万（吉力士）GLS系列Versaflex TPE G2708N 是一种一种容易加工的通用型TPE,设计用于广泛的各种用途,包括必须符合FDA标准的应用,手握时不打滑 ,可以重叠模塑方式粘接在聚丙烯上,手
-
PBT(聚对苯二甲酸丁二醇酯)1300|惠州南亚|物性表参数
南亚塑胶工业（惠州）(Nan Ya Plastic)PBT 1300是一种阻燃聚对苯二甲酸丁二醇酯(PBT)树脂，产品用途:用于连接器、插座、开关、端子台等。以下是PBT(聚對苯二甲酸丁二醇酯)1300|惠州南亚|物性表参数机械性能额定值单位测试方法拉伸强度600Kg/cmASTM D638弯曲弹性率30000Kg/cmASTM D790缺口冲击强度4kg.cm/cmASTM D256热性能额
-
PET(聚对苯二甲酸乙二醇酯)RE5329|陶氏杜邦|物性表参数
陶氏杜邦RYNITE PET RE5329是一款加36%玻璃增强PET,开发用于挤压和注射成型产品,杜邦为塑料行业提供一系列材料科学生产、创新设计和实际经验支持行业发展,我们凭借在聚合物科学领域的丰富经验推动市场创新，并致力为客户解决问题,如今，您需要从供应商得到的不仅只是材料，您需要一种资源，支持您的项目从概念到商业应用等层
-
TPE/G7980-9001-02/TPE物性表参数
美国普立万（吉力士）GLS系列Dynaflex TPE G7980-9001-02 是一种容易加工的通用型 TPE，硬度是80A,设计用于广泛的各种用途，包括必须符合FDA标准的应用,手握时不打滑, 可以重叠模塑方式粘接
-
PC(聚碳酸酯)PC-1150R/韩国乐天化学/物性表参数
韩国乐天化学的LOTTE Chemical HOPELEX PC PC-1150R 是一种聚碳酸脂塑料(Polycarbonate)，特性是低粘度、离型性优异、FDA/EU 食品容器认证，用于普通注塑产品。 以下是PC(聚碳酸酯)PC-1150R/韩国乐天化
-
Lexan/PC/EXL1132T物性表参数
SABIC 沙伯基础创新Lexan PC EXL1132T 物性表参数 塑炜供应SABIC沙伯基础创新Lexan PC EXL1132T，提供SABIC公司的各种工程塑料物性表，塑胶物性大全，所有PC塑料物性表，塑料物性大全，是中国最
-
PC(聚碳酸酯)NH3025NP/Samyang(三养)物性表参数
Samyang(三养)TRIREX PCNH3025NP是一种非强化,阻燃 (V0, 5VB)聚碳酸酯，比重是1.20g/cm³，熔流率（熔体流动速率）(300°C/1.2 kg)20g/10min，有着优异的机械特性，很好的尺寸稳定性及良好的电气特性，应用于电子电器。以下是PC(聚碳酸酯)NH3025NP/Samyang(三养)物性表参数PROPERTYUNITASTM METHODTYPICAL DATAPhysic
-
PBT(聚对苯二甲酸丁二酯)5820G30H|三菱工程塑料|物性表参数
三菱工程塑料NOVADURAN PBT 5820G30H是一种聚对苯二甲酸丁二酯(PBT合金)材料，熔融体积流量（MVR)(cm³/10min)是30((250°C/5.0kg))，简支梁缺口冲击强度(kJ/m²)是7.0(23°C)，含有的填充物为30%玻璃纤维增强材料，加工方式为：注射成型，NOVADURAN 5820G30H主要特性为:高强度/抗翘曲。以下是PBT(聚对苯二甲酸丁二酯)5
-
PC(聚碳酸酯)302-7|盛禧奥(TRINSEO)物性表参数
盛禧奥(TRINSEO)的CALIBRE PC 302-7树脂是一种应用于实体片材挤出的标准的线性聚碳酸酯树脂。CALIBRE 302-7含有紫外线吸收剂添加剂，但是请注意室外应用的片材还需要一个防紫外线的保护层,建议使用CALIBRE 320UV进行共挤出，以制备出一个厚度为50µm的UV防护层.。CALIBRE PC 302-7物性表参数PDF文档浏览生产商：(TRIN
-
ForTii(荷兰帝斯曼)XS51/PA4T(尼龙4T)物性表参数
荷兰帝斯曼ForTii XS51 PA4T 是加阻燃剂, 不含卤素和红磷, 玻纤增强的尼龙4T材料,ForTii突破性的高温聚酰胺，无卤阻燃牌号可用于电子、照明、汽车、白色家电、航空等行业中严苛的应用。