LEXAN(沙伯基础)505R/PC(聚碳酸酯)物性表参数
沙伯基础SABIC塑料LEXAN 505R聚碳酸酯（PC）是一种可注射成型的非氯化和非溴化阻燃级，填充10％玻璃纤维, 它具有UL94 V0@1.5mm的额定值，并提供各种不透明颜色选项, 这是LEXAN 500,500R，500RS，500ECR的替代品。
 |
沙伯基础SABIC塑料LEXAN 505R PC物性表参数PDF文档下载 |
以下是LEXAN(沙伯基础)505R/PC(聚碳酸酯)物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 63 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 12 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3930 | MPa | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 108 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3530 | MPa | ASTM D 790 | |
| Hardness, Rockwell M | 85 | - | ASTM D 785 | |
| Hardness, Rockwell R | 124 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 11 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3400 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 115 | MPa | ISO 2039-1 | |
| IMPACT | ||||
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 107 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 61 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | 130 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 15 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Specific Heat | 1.21 | J/g-°C | ASTM C 351 | |
| Thermal Conductivity | 0.2 | W/m-°C | ASTM C177 | |
| Vicat Softening Temp, Rate B/50 | 149 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 143 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.68E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.46E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.21 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 141 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 144 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Ae | |
| HDT/Ae, 1.8 MPa Annealed 120°C, 2hrs | 136 | °C | ISO 75/Ae | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Bf | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.26 | - | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 | |
| Water Absorption, 24 hours | 0.12 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.31 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 7 | g/10 min | ASTM D 1238 | |
| Density | 1.25 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.31 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm³/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 33 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94-5VA Flame Class Rating | 3 | mm | UL 94 | |
| UL Compliant, 94-5VB Rating | 2 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Oxygen Index (LOI) | 37 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 290-320 | °C | ||
| Nozzle Temperature | 280-310 | °C | ||
| Front - Zone 3 Temperature | 290-320 | °C | ||
| Middle - Zone 2 Temperature | 280-310 | °C | ||
| Rear - Zone 1 Temperature | 270-300 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 80-120 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：7777 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：7410 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：6191 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：6024 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：5509 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：5035 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：4703 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：4463 -
COC(环烯烃共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一种烯烃聚合物(COP)具有优异的光学性能，可用于制造相机和激光打印机的光学部件，比重是1.01g/cm(ASTM D792)，熔流率（熔体流动速率）(280C/2.16 kg)是25g/10 min，ZEO
浏览量：4441 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：4282 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：4272 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：4264 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：4143 -
PC(聚碳酸酯)PC-1100|乐天化学(LOTTE CHEMI···乐天化学的LOTTE Chemical HOPELEX PC PC-1100 是一种聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高强度、FDA/EU 食品容器认证，用于普通注塑产品。 以下是PC(聚碳酸酯)PC-1100/韩国乐天化学
浏览量：4048 -
Grilamid(瑞士EMS)TR55|PA12(尼龙12)物性表···瑞士(EMS)Grilamid PA12 TR55是一种基于十二内酰胺的高性能热塑性材料，经验证可用于众多高品质应用，并且已拥有40多年的应用经验。这些应用包括精密注塑成型（例如电子应用中的）、卫生洁具、燃油和空气制动系统管路及光纤波导护套,Grilamid TR等级是一种无定形热塑性塑料，其成分以一种独特方式组合了半结晶聚酰胺12和无定
浏览量：3976
推荐文章
-
TPE(热塑性弹性体)TC3SCE/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TC3SCE 是一款耐刮擦TPE,硬度是27A的SCR系列自然色TPE材料,用于要求高耐刮擦性应用的材料解决方案。该系列特征之一是舒适的触感，典型应用：功能和设计要素
-
LCP/H130/LCP物性表参数
LCP H130 物性表参数介绍如下： Celanese VECTRA H130 ( 液晶聚合物 -LCP 塑料 ) 本物性表由 www.cn-plas.com 塑料网提供，转载请注明来源！ Physical Properties 物理性质 Metric 公制数据 English 英制数据
-
PA66(尼龙66)ECO315J|奥升德(泛达)物性表参数
奥升德VYDYNE PA66 ECO315J是一种无卤、无填充、阻燃的PA66/6共聚物，具有优异的韧性和延展性，它是稳定的，提供热稳定性高达125°C，在干燥的环境下1000小时，ECO315J BK0707也为机械进给和易于模具释放润滑，并有一个UL 94易燃等级的V-0在0.4毫米(0.016")厚。奥升德VYDYNE PA66 ECO315J物性表参数PDF文档下载以下是P
-
TPE(热塑性弹性体)TF6FMA/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TF6FMA 是一款自然色, 硬度60A,用于食品接触应用的材料解决方案，能提供卓越的 PC、ABS 及PETG 等极性热塑性材料包胶性能,典型应用:剃须刀、功能和设计要素、
-
PP(聚丙烯)RP2965/利安德巴塞尔/物性表参数
利安德巴塞尔(Lyondellbasell)Moplen PP RP2965是一种聚丙烯无规共聚物，熔体流动速率(230°C/2.16kg)是20克/10分钟，密度(23°C)是0.9克/厘米³，mopeln RP2965适用于注塑应用，也可用于技术化合物，它具有中等熔体流动速率，并以颗粒形式供应。以下是PP(聚丙烯)RP2965/利安德巴塞尔/物性表参数基本信息特性刚性，良好良
-
PP(聚丙烯)S1005/台化(TAIRIPRO)物性表参数
台化(TAIRIPRO)PP S1005是一种扁纱级聚丙烯，比重是0.900g/cm³，熔流率（熔体流动速率）(230°C/2.16 kg)是5.0g/10min，特点是延伸性佳 、加工性佳，应用于文件夾、吸管 。以下是PP(聚丙烯)S1005/台化(TAIRIPRO)物性表参数基本信息黄卡编号E162823-100769101特性均聚物机构评级EC 1907/2006 (REACH)FDA 21 CFR 177.1520RoH
-
PA66(尼龙66)70GB30HSL/陶氏杜邦/物性表参数
陶氏杜邦PA66 70GB30HSL是一种聚酰胺66，加30%玻璃纤维增强，性能是热稳定，抗水解，颜色是NC010，BK099。原材料生产商：DuPont（陶氏杜邦）以下是PA66(尼龙66)70GB30HSL/陶氏杜邦/物性表参数物理性能干燥调节后的单位制测试方法密度 1.37--g/cm³ISO 1183收缩率 ISO 294-4 垂直流动方向1.0--%ISO
-
ABS(丙烯腈-丁二烯-苯乙烯共聚物)ANC120|台化|物性表参数
台化TAIRILAC ABS ANC120是一种防火级别的丙烯腈-丁二烯-苯乙烯共聚物，性能是阻燃，MI(220℃×10kg): 6.4、Izod (ASTM,1/4"): 28、FM(ASTM): 23000、TS(ASTM): 400，应用于防火级材料、电视外壳、电脑外壳、 事务机外壳。以下是ABS(丙烯腈-丁二烯-苯乙烯共聚物)ANC120|台化|物性表参数物理性能额定值单位制测试方法密
-
Bayblend(拜本兰)FR3010IF|科思创(PC/ABS合金)物性表参数
科思创Bayblend PC/ABS FR3010IF 是加阻燃,;维卡软化点温度/ B 120 = 108C;耐热性增加;UL认可94 5VB (1.5 mm);灼热丝温度(GWFI):在2.0毫米960C. PC/ABS是聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，
-
POK(脂肪族聚酮)M330S|晓星(POKETONE)物性表参数
晓星(POKETONE)POK M330S是一种抗UV注塑成型脂肪族聚酮树脂，是能够使用于汽车燃油输送管路、内外部装修材料、电子电器部件、气体阻隔包装材料、管子等多种用途的ENPLA材料。以下是POK(脂肪族聚酮)M330S|晓星(POKETONE)物性表参数物理性能额定值单位制测试方法比重 1.24g/cm³ASTM D792熔流率（熔体流动速率） (240°C/2.16