沙伯基础创新塑料SABIC的VALOX PDR4922 PBT是一种加GF填充PBT，水解稳定，冲击改性，高流动，汽车连接器。

以下是VALOX(沙伯基础)PDR4922/PBT热塑性聚酯/物性表参数

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	85	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	81	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	2.4	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	3.3	%	ASTM D 638
Tensile Modulus, 50 mm/min	5410	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	133	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	4580	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	85	MPa	ISO 527
Tensile Stress, break, 50 mm/min	81	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3	%	ISO 527
Tensile Strain, break, 50 mm/min	3.6	%	ISO 527
Tensile Modulus, 1 mm/min	5230	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	130	MPa	ISO 178
Flexural Modulus, 2 mm/min	4860	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	102	J/m	ASTM D 256
Izod Impact, notched, -30°C	58	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	8	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	10	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	6	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	8	kJ/m²	ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50	200	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	216	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	184	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.18E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.14E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	4.39E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.18E-04	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	195	°C	ISO 306
Vicat Softening Temp, Rate B/120	196	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	170	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.4	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.16	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.94	%	SABIC method
Melt Flow Rate, 250°C/2.16 kgf	13.4	g/10 min	ASTM D 1238
Density	1.4	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.03	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.03	%	ISO 62
Melt Volume Rate, MVR at 250°C/2.16 kg	12	cm³/10 min	ISO 1133
Injection Molding
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 265	°C
Nozzle Temperature	245 - 260	°C
Front - Zone 3 Temperature	250 - 265	°C
Middle - Zone 2 Temperature	245 - 260	°C
Rear - Zone 1 Temperature	240 - 255	°C
Mold Temperature	50 - 75	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 100	rpm
Shot to Cylinder Size	40 - 80	%
Vent Depth	0.025 - 0.038	mm

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：VALOX(沙伯基础)K4560/PBT热塑性聚酯/物性表参数下一页：VALOX(沙伯基础)SHF4320/PBT热塑性聚酯/物性表参数

返回首页返回物性参数列表

VALOX(沙伯基础)PDR4922/PBT热塑性聚酯/物性表参数

热门文章

推荐文章