PA6(尼龙6)BKV140/德国朗盛/物性表参数

日期：2020-04-25 02:25:59 编辑：科思德塑胶来源：科思德塑胶浏览：304

德国朗盛LANXESS Durethan PA6 BKV140是一种加40%玻璃纤维，注塑，提高流动性，表面光洁度，低翘曲倾向树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV140

生产商：LANXESS(德国朗盛)、品名：Durethan
PA6(尼龙6)BKV140/德国朗盛/物性表参数

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 290 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.16
	Molding shrinkage, transverse	150x105x3; 290 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.71
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.03
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.1
	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.1
	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	11500	6700
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	180	120
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	6.0
	Tensile creep modulus	1 h	MPa	ISO 899-1		6100
	Tensile creep modulus	1000 h	MPa	ISO 899-1		4900
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	100	110
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	95	95
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	25	30
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	10	10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	80	90
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	75	75
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	20	30
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	16	16
	Flexural modulus	2 mm/min	MPa	ISO 178-A	10400	6200
	Flexural strength	2 mm/min	MPa	ISO 178-A	295	175
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	280	145
	Puncture maximum force	23 °C	N	ISO 6603-2	1175	1450
	Puncture maximum force	-30 °C	N	ISO 6603-2	975	1000
	Puncture energy	23 °C	J	ISO 6603-2	3.8	5.2
	Puncture energy	-30 °C	J	ISO 6603-2	2.3	2.3
	Ball indentation hardness		N/mm²	ISO 2039-1	200
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	213
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	210
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	22
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302			ISO 3795	passed
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 200
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.0	10
	Relative permittivity	1 MHz	-	IEC 60250	4.0	5.0
	Dissipation factor	100 Hz	10-4	IEC 60250	70
	Dissipation factor	1 MHz	10-4	IEC 60250	200
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E09
	Surface resistivity		Ohm	IEC 60093	1E14	1E10
	Electric strength	1 mm	kV/mm	IEC 60243-1	40	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	575
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	450 M - 0.6
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.6
	Density		kg/m³	ISO 1183	1460
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-290
	Mold temperature		°C	-	80-100