VALOX(沙伯基础)VX4920/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX VX4920 PBT是一种加20%玻璃增强有核PBT/ASA共混物，具有优异的机械性能、高维稳性和低密度,应用领域:连接器及汽车工业。
 |
沙伯基础创新塑料的VALOX VX4920 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)VX4920/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 105 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 105 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7200 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 160 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 160 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5500 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 80 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 155 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 4 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5700 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 130 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 118 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 40 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 680 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 605 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 70 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 10 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 8 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 210 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 170 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.25 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.86E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.67E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 3.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.05E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.38E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.57E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 165 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 209 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 179 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 170 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.38 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.4 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.4-0.8 | % | SABIC method | |
| Melt Flow Rate, 200°C/3.8 kgf | 17 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 35 | g/10 min | ASTM D 1238 | |
| Density | 1.38 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.76 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.27 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 17 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 175 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 24 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 | |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 24 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0024 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.4 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：14086 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：11911 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：11417 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：9513 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：8387 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：8252 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7785 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：7303 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：7171 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6832 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6793 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6632 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：6512 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：6476 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6428
推荐文章
-
POM(聚甲醛树脂)GN705|旭化成|物性表参数
旭化成(AsahiKASEI)TENAC(铁耐克)POM GN705是加25%玻纤增强具有高刚性和极佳的尺寸稳定性的聚甲醛树脂，密度 1.59(g/cm³)，弯曲模量8500(MPa) ，简支梁缺口冲击强度7.0(kJ/m²) ，典型用途领域包括工程/工业配件、房屋和汽车行业。TENAC GN705 POM物性表参数PDF文档下载以下是POM(聚甲醛树脂)GN705|旭化成|物性表参数物理
-
PP(聚丙烯聚合物)SFC-750/乐天化学/物性表参数
乐天化学(LOTTE CHEMICAL)PP SFC-750是一种聚丙烯聚合物，比重(23°C)是0.9克/厘米³，熔体流动速率(230°C/2.16kg)是8克/10分钟，该等级专为铸膜技术而设计，它具有出色的清晰度和光泽度，非常低的雾霾，广泛的热粘范围和120°C的低密封起始温度，它是专为高质量的包装应用，作为热封层薄膜，RANPELEN SFC-750是易于加工
-
PC(聚碳酸酯)LV-2250Y|嘉兴帝人|物性表参数
嘉兴帝人Panlite PC LV-2250Y是一款熔融体积流量是8MVR cm/10min，特性是脱模性能良好; 中等粘性，通用级别的塑胶原材料，LV-2250Y在耐冲击性、耐热性、尺寸稳定性、电学特性、透明性以及卫生性能等诸多方面具有其突出的优点，现被广泛应用于电子电器、办公用品、精密机械、汽车、安保及家庭用品等众多领域。嘉兴帝人Panlit
-
PPS（聚苯硫醚）R-4-06/菲利浦/物性表参数
Chevron Phillips 菲利普 PPS R-4-06 物性表参数 PPS R-4-06 是美国雪佛龙菲利普工程塑料聚苯硫醚 PPS 系列 Ryton 型号之一 为您提供美国雪佛龙菲利普耐高温工程塑料聚苯硫醚 PPS R-4-06 的中英文物
-
POM(聚甲醛)100T|DuPont(陶氏杜邦)物性表参数
陶氏杜邦DuPont DELRIN POM 100T 是一种增韧高粘度同聚物,通常用于要求应用在汽车、家用电器、体育、工业工程、电子、和消费品行业,也有良好的尺寸稳定性和良好的电绝缘,它们具有天然的弹性，自润滑，并可用于各种颜色和特殊等级，陶氏杜邦DuPont POM 100T 的熔流率（熔体流动速率）(190°C/2.16 kg)12g/10min、
-
PBT(聚对苯二甲酸丁二酯)5010G30X4|三菱工程塑料|物性表参数
三菱工程塑料NOVADURAN PBT 5010G30X4是一种聚对苯二甲酸丁二酯(PBT)材料，熔融体积流量（MVR)(cm³/10min)是30((250°C/5.0kg))，简支梁缺口冲击强度(kJ/m²)是10.0(23°C)，含有的填充物为30% 玻璃纤维增强材料，加工方式为：注射成型，NOVADURAN 5010G30X4主要特性为:阻燃/额定火焰。以下是PBT(聚对苯二甲酸丁二酯
-
塞拉尼斯TPV 111-73|Santoprene 111-73物性表参数
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 111-73是一种热塑性硫化弹性体，它也是一种坚硬、黑色、通用的热塑性硫化胶(TPV)，这种材料结合了良好的物理性能和耐化学性，在广泛的注射成型应用中使用，这种级别的山托丁烯TPV是剪切依赖的，可以在传统的热塑性塑料设备上进行注射成型加工。以下是塞拉尼斯TPV 111-73|Santopr
-
SPS(间规聚苯乙烯)SP130|出光兴产|物性表参数
出光兴产的XAREC SPS SP130 是间规聚苯乙烯树脂，密度是1.18g/cm，拉伸模量是3200MPa，简支梁缺口冲击强度(23C)4kJ/m，UL阻燃等级 ( 1.500mm) HB UL94，因分子规则排列，应用于汽车,电子用途，故与以
-
PC(聚碳酸酯)2665/科思创(Makrolon)物性表参数
科思创(Covestro)模克隆(Makrolon) PC 2665 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 12cm cm /10 min，中粘度，含有脱模剂，阻燃UL 94V-2/1.5 mm和3.0 mm，应用于透明通用产品。 以下是PC(聚碳
-
PA46(尼龙46)HFX31SW|恩骅力(Envalior)物性表参数
恩骅力(Envalior)(原帝斯曼DSM)Stanyl聚合物PA46 HFX31SW是一款加20% 玻纤增强, 高流动性, 不含卤素和红磷，注塑成型的PA46原料，应用于USB-C连接器，Stanyl作为高性能聚酰胺,在对耐热性、设计硬度、摩擦磨耗以及流动性都有要求的严苛的应用中表现优异，Stanyl能在高达220℃时依旧保持良好的机械性能，这使它比PPA、PA6T、P