PA66(尼龙66)AKV30FN04德国朗盛/物性表参数

日期：2020-04-25 02:56:12 编辑：科思德塑胶来源：科思德塑胶浏览：507

德国朗盛Durethan PA66 AKV30FN04是一种PA66,加30%玻璃纤维，注塑尼龙树脂,根据特定的材料及所需等级，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。

PA66 AKV30FN04物性表参数PDF文档下载

生产商：LANXESS(德国朗盛)、品名：Durethan
PA66(尼龙66)AKV30FN04德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
C	Molding shrinkage, parallel	60x60x2; 270 °C / WZ 80 °C; 600 bar	%	ISO 294-4	0.3
C	Molding shrinkage, transverse	60x60x2; 270 °C / WZ 80 °C; 600 bar	%	ISO 294-4	0.8
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	10500	6500
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	138	87
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.9	5.7
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	65	70
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	60	60
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	11
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	55	65
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	50	55
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	12
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A		<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	10100	6300
	Flexural strength	2 mm/min	MPa	ISO 178-A	230	150
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.2	5.5
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		135
	Ball indentation hardness		N/mm²	ISO 2039-1	207
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	260
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	230
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	250
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	233
C	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
C	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
C	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
C	Burning behavior UL 94	0.4 mm	Class	UL 94	V-0
C	Burning behavior UL 94-5V	1.5 mm	Class	UL 94	5VA
C	Oxygen index	Method A	%	ISO 4589-2	34
	Resistance to heat (ball pressure test)		°C	IEC 60695-10-2	233
	Glow wire test (GWFI)	0.4 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.4 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	750
Electrical properties (23 °C/50 % r. h.)
C	Volume resistivity		Ohm·m	IEC 60093	5.00E+13
C	Surface resistivity		Ohm	IEC 60093	3.00E+16
C	Electric strength	1 mm	kV/mm	IEC 60243-1	41
C	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
	Comparative tracking index CTI	Solution A	PLC	UL 746A	0
Other properties (23 °C)
C	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	4.4
C	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.4
C	Density		kg/m³	ISO 1183	1420
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	270
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.07
	Melt temperature (Tmin - Tmax)		°C	-	265-285
	Mold temperature		°C	-	80-100

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

德国朗盛Durethan PA66 AKV30FN04具有高抗震及抗裂性能，具体指标与材料的等级与含水量有关。弹性体改性的材料即使在低含水量及低温下也具有良好的韧性,硬度高，尤其对于玻纤增強级别产品；拉伸模量：1,300 到 15,700 MPa (取决于含水量),良好的机械性能及阻尼吸声效应、低摩擦力、急速运行能力好，气体阻隔性能好（薄膜级）,

密度	1.01~1.23	模具温度	80.0 到 100°C
加工（熔体）温度	260 到 270°C	注射压力	230 到 250°C
预热	温度/°C	130°C	工艺参数	注射时间	20~90
时间/h	4.0hr	高压时间	0~5
料桶温度/°C	后段	193 到 238°C	冷却时间	20~90
中段	210 到 249°C	总周期	220 到 260°C
前段	221 到 254°C	螺杆转数	30 到 60rpm
喷嘴温度	232 到 274°C	使用注射机类型	螺杆式

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA66(尼龙66)AKV30/德国朗盛/物性表参数下一页：PA66(尼龙66)AKV30FN04LT/德国朗盛/物性表参数

返回首页返回物性参数列表